4
Figure 2
Compression modulus (D (t)) – time, aggregate diameter of 4.75 - 9.50 mm (Small, S), 9.50 - 12.50 mm
(Medium, M) and 12.50 - 19.00 mm (Large, L), the amount of natural rubber (Rubber, R) 0 % wt, the speed of the
compression (Speed) at 50 mm/min and the time at 0 min for mastication (Masticate).
Figure 3
Stress
-
Cauchy’s deformation, aggregate diameter of 4.75 - 9.50 mm (Small, S), 9.50 - 12.50 mm (Medium,
M) and 12.50 - 19.00 mm (Large, L), the amount of natural rubber (Rubber, R) 0 % wt, the speed of the compression
(Speed) at 150 mm/min and the time at 0 min for mastication (Masticate).
Figure 4
Compression modulus (D (t)) – time, aggregate diameter of 4.75 - 9.50 mm (Small, S), 9.50 - 12.50 mm
(Medium, M) and 12.50 - 19.00 mm (Large, L), the amount of natural rubber (Rubber, R) 0 % wt, the speed of the
compression (Speed) at 150 mm/min and the time at 0 min for mastication (Masticate).